產品名稱：耐諾碳化鎢珠NanorWC
產品鏈接：http://www.las-vegas-bachelor-party.com/Products-7724106.html
手機版鏈接：http://m.atobo.com/Products/7724106.html
耐諾碳化鎢珠(NanorWC）
耐諾碳化鎢珠NanorWC由專利的的滴定滾動工藝成型，在真空電爐中無氧燒結而成。致密的晶相結構造就了珠子至高的密度和耐磨性，是研磨介質微珠行業革命性的創造。
碳化鎢含量: 90%,              氧化鈷含量: 10%,
比      重: >14.5kg/dm3,      散      重: >8.6kg/L,
莫 氏 硬度: 9.5,              維 氏 硬度: >1500kg/mm2,
斷 裂 韌性: 15Mpa.m1/2      彈 性 模量: >710Gpa,
粒      徑: 0.2-2.2mm,      顏      色: 黑色,         
Nanor-WC tungsten carbide bead is shaped with cutting edge dropping & rolling
method and is sintered in the vacuum kiln. The compact microstructure of bead offer
the bead the highest density and wear resistance. It is a creative invention of grinding
media special in small sizes.
WC %: 90 ,                          Co %: 10
Density: >14.5kg/dm3,              Bulk Density: >8.6kg/L
Hardness Vickers: >1500kg/mm2,      Elasticity Module: >710GPa1/2 
Crushing Strength: 2000N (2mm)，    Sizes: 0.2-2.2mm ,